Neodymium iron boron ( NdFeB) is a type of rare earth magnetic material.
NdFeB is the most advanced commercialized permanent magnet material available today.
This material has similar properties as the samarium cobalt except that it is more easily oxidized
and generally doesn't have the same temperature resistance.
However, NdFeB magnets have the highest energy products approaching 52MGOe and are mechanically
stronger than samarium cobalt magents. NdFeB material is more costly by weight than ceramic or alnico
but produces the highest amount of flux per unit of volume or mass amking it very economical for
many applicantions. Their high energy products lend themselves to comnpact designs
Neodymium iron boron ( NdFeB) is a type of rare earth magnetic material.
NdFeB is the most advanced commercialized permanent magnet material available today.
This material has similar properties as the samarium cobalt except that it is more easily oxidized
and generally doesn't have the same temperature resistance.
However, NdFeB magnets have the highest energy products approaching 52MGOe and are mechanically
stronger than samarium cobalt magents. NdFeB material is more costly by weight than ceramic or alnico
but produces the highest amount of flux per unit of volume or mass amking it very economical for
many applicantions. Their high energy products lend themselves to comnpact designs
Plating Type<o:p> | Overall Thickness<o:p> | Salt Spray Test<o:p> | Pressure Cooker Test<o:p> |
NiCuNi (Nickel Copper Nickel)<o:p> | 15-21 μm<o:p> | 24 hours<o:p> | 48 hours<o:p> |
NiCu + Black Nickel<o:p> | 15-21 μm<o:p> | 24 hours<o:p> | 48 hours<o:p> |
NiCuNi + Epoxy<o:p> | 20-28 μm<o:p> | 48 hours<o:p> | 72 hours<o:p> |
NiCuNi + Gold<o:p> | 16-23 μm<o:p> | 36 hours<o:p> | 72 hours<o:p> |
NiCuNi + Silver<o:p> | 16-23 μm<o:p> | 24 hours<o:p> | 48 hours<o:p> |
Zinc<o:p> | 7-15 μm<o:p> | 12 hours<o:p> | 24 hours<o:p> |
Welcome to contact us ,we are 24 hours on line,Ms Wu is at your service:
Cell phone:86+13855156049 86+18009691660
Skype:rainbow0051
We will reply your email or fax within 24 hours.
Plating Type<o:p> | Overall Thickness<o:p> | Salt Spray Test<o:p> | Pressure Cooker Test<o:p> |
NiCuNi (Nickel Copper Nickel)<o:p> | 15-21 μm<o:p> | 24 hours<o:p> | 48 hours<o:p> |
NiCu + Black Nickel<o:p> | 15-21 μm<o:p> | 24 hours<o:p> | 48 hours<o:p> |
NiCuNi + Epoxy<o:p> | 20-28 μm<o:p> | 48 hours<o:p> | 72 hours<o:p> |
NiCuNi + Gold<o:p> | 16-23 μm<o:p> | 36 hours<o:p> | 72 hours<o:p> |
NiCuNi + Silver<o:p> | 16-23 μm<o:p> | 24 hours<o:p> | 48 hours<o:p> |
Zinc<o:p> | 7-15 μm<o:p> | 12 hours<o:p> | 24 hours<o:p> |