N33, N35, N38, N40, N42, N48, N50, N52 (M, H, SH, EH, UH,AH)
piece Sintered N40 blokc ndfeb magnets
1 Sintered N40 blokc ndfeb magnets
Items | Neodymium magnet raw material | |
Material | neodymium-iron-boron | |
Shape available | Disc,Cylinder,Block,Ring,Countersunk,Segment,Trapezoid,Irregular shapes and more;More shapes can be customized. | |
Coating | Ni-Cu-Ni,Nickel,Zinc,Gold,Silver,Epoxy and more. | |
Working Temperature | Grade | Temp.Coefficient |
N35-N52 | 80°C (176°F) | |
N35M-N45M | 100°C (212°F) | |
N33H-N42H | 120°C (248°F) | |
N30SH-N40SH | 150°C (302°F) | |
N28UH-N35UH | 180°C (356°F) | |
N28EH-N38EH | 180°C (356°F) | |
N30AH-N33AH | 220°C (428°F) | |
Technology | We have advanced R&D center,quality control and professional machining technicians. | |
Application | Neodymium magnet raw magnetrials are widely used in industrial field, such as speaker,louder speaker,sensor,motor,alternator ect; And also it is popular in ladies bags,purses,shoes,crafts and jewelry ect. |
Items | Neodymium magnet raw material | |
Material | neodymium-iron-boron | |
Shape available | Disc,Cylinder,Block,Ring,Countersunk,Segment,Trapezoid,Irregular shapes and more;More shapes can be customized. | |
Coating | Ni-Cu-Ni,Nickel,Zinc,Gold,Silver,Epoxy and more. | |
Working Temperature | Grade | Temp.Coefficient |
N35-N52 | 80°C (176°F) | |
N35M-N45M | 100°C (212°F) | |
N33H-N42H | 120°C (248°F) | |
N30SH-N40SH | 150°C (302°F) | |
N28UH-N35UH | 180°C (356°F) | |
N28EH-N38EH | 180°C (356°F) | |
N30AH-N33AH | 220°C (428°F) | |
Technology | We have advanced R&D center,quality control and professional machining technicians. | |
Application | Neodymium magnet raw magnetrials are widely used in industrial field, such as speaker,louder speaker,sensor,motor,alternator ect; And also it is popular in ladies bags,purses,shoes,crafts and jewelry ect. |
Plating Type | Overall Thickness | Salt Spray Test | Pressure Cooker Test |
NiCuNi (Nickel Copper Nickel) | 15-21 μm | 24 hours | 48 hours |
NiCu + Black Nickel | 15-21 μm | 24 hours | 48 hours |
NiCuNi + Epoxy | 20-28 μm | 48 hours | 72 hours |
NiCuNi + Gold | 16-23 μm | 36 hours | 72 hours |
NiCuNi + Silver | 16-23 μm | 24 hours | 48 hours |
Zinc | 7-15 μm | 12 hours | 24 hours |
Plating Type | Overall Thickness | Salt Spray Test | Pressure Cooker Test |
NiCuNi (Nickel Copper Nickel) | 15-21 μm | 24 hours | 48 hours |
NiCu + Black Nickel | 15-21 μm | 24 hours | 48 hours |
NiCuNi + Epoxy | 20-28 μm | 48 hours | 72 hours |
NiCuNi + Gold | 16-23 μm | 36 hours | 72 hours |
NiCuNi + Silver | 16-23 μm | 24 hours | 48 hours |
Zinc | 7-15 μm | 12 hours | 24 hours |