Ferrite magnets are manufactured mainly of strontium or barium ferrites and iron oxide. Hard Ferrite (Ceramic)
magnets are produced as Isotropic and Anisotropic types. Isotropictype magnets are produced without orientation
and can be magnetized in any direction. On the other hand,Anisotropic magnets are exposed to an electromagnetic field
during their process to achieve higher magnetic energy and properties. This is done by pressing dry powders or slurry into
a desired die cavity with or without orientation. After the compaction into the dies the parts are exposed to a high temperature,
a process known as sintering. This process allows them to hold the shape of the part and gives them mechanical and magnetic
strength, and produces hard brittle parts. Because of their physical strength they should not be used as a structural part in any
assembly. The grinding process using diamond grinding wheels allows for close dimensional tolerances.
Ferrite (Ceramic) magnets have good resistance to demagnetization and with their high Curie temperature they have
excellent high working temperatures and most of all they have excellent resistance to corrosion. Ferrite (Ceramic) magnets
are excellent choices for many applications due to their economical low price and abundance of raw materials and they
do not fluctuate much in price.
They are the most widely used magnets in a wide range of applications. Ferrite (Ceramic) magnets come in a variety of shapes;
round, square, rectangular, arc segments, triangle, rings and special shapes.
Ferrite magnets are manufactured mainly of strontium or barium ferrites and iron oxide. Hard Ferrite (Ceramic)
magnets are produced as Isotropic and Anisotropic types. Isotropictype magnets are produced without orientation
and can be magnetized in any direction. On the other hand,Anisotropic magnets are exposed to an electromagnetic field
during their process to achieve higher magnetic energy and properties. This is done by pressing dry powders or slurry into
a desired die cavity with or without orientation. After the compaction into the dies the parts are exposed to a high temperature,
a process known as sintering. This process allows them to hold the shape of the part and gives them mechanical and magnetic
strength, and produces hard brittle parts. Because of their physical strength they should not be used as a structural part in any
assembly. The grinding process using diamond grinding wheels allows for close dimensional tolerances.
Ferrite (Ceramic) magnets have good resistance to demagnetization and with their high Curie temperature they have
excellent high working temperatures and most of all they have excellent resistance to corrosion. Ferrite (Ceramic) magnets
are excellent choices for many applications due to their economical low price and abundance of raw materials and they
do not fluctuate much in price.
They are the most widely used magnets in a wide range of applications. Ferrite (Ceramic) magnets come in a variety of shapes;
round, square, rectangular, arc segments, triangle, rings and special shapes.
High Grade Arc Magnet
Product: | Ferrite magnetic disc | ||||
Certificates: | ISO9001,CE,ROHS,SGS | ||||
Shapes: | Ring, disk, block, segment, ball, cylinder and so on; customized made. | ||||
Advantages: | 1.recoil permeability 2.high coercive force 3.relatively low specific density 4.economical cost | ||||
Features: | 1.good anti-corrosion performance 2.no surface treatment needed 3.isotropic & anisotropic magnets | ||||
Magnetic Performance | |||||
Grade | Remanence Br mT (kGs) | Coercive force HcB KA/m (KOe) | Magnetic energy product Max KJ/m3 MGOe | Equivalents | |
Y10T | 200-218 | 125-145 | 6.5-8.0 | C1 | |
2.00-2.18 | 1.57-1.82 | 0.8-1.0 | |||
Y25 | 360-370 | 135-150 | 22.5-25.3 | ||
3.60-3.70 | 1.70-1.88 | 2.8-3.2 | |||
Y30 | 380-390 | 191-210 | 27-30 | ||
3.80-3.90 | 2.40-2.64 | 3.4-3.7 | |||
Y33 | 400-410 | 175-195 | 30.0-31.5 | C5 | |
4.00-4.10 | 2.20-2.45 | 3.8-4.0 | |||
Y35 | 410-420 | 220-235 | 31.5-33.0 | ||
4.10-4.20 | 2.77-2.95 | 4.0-4.2 | |||
Y30BH | 380-390 | 223-235 | 27.0-30.0 | C8 | |
3.80-3.90 | 2.80-2.95 | 3.4-3.7 | |||
Y33BH | 400-410 | 288-300 | 30.4-31.5 | ||
4.00-4.10 | 3.62-3.77 | 3.8-4.0 |
Welcome to contact us ,we are 24 hours on line,Ms Wu is at your service:
Cell phone:86+13855156049 86+18009691660
Skype:rainbow0051
We will reply your email or fax within 24 hours.
High Grade Arc Magnet
Product: | Ferrite magnetic disc | ||||
Certificates: | ISO9001,CE,ROHS,SGS | ||||
Shapes: | Ring, disk, block, segment, ball, cylinder and so on; customized made. | ||||
Advantages: | 1.recoil permeability 2.high coercive force 3.relatively low specific density 4.economical cost | ||||
Features: | 1.good anti-corrosion performance 2.no surface treatment needed 3.isotropic & anisotropic magnets | ||||
Magnetic Performance | |||||
Grade | Remanence Br mT (kGs) | Coercive force HcB KA/m (KOe) | Magnetic energy product Max KJ/m3 MGOe | Equivalents | |
Y10T | 200-218 | 125-145 | 6.5-8.0 | C1 | |
2.00-2.18 | 1.57-1.82 | 0.8-1.0 | |||
Y25 | 360-370 | 135-150 | 22.5-25.3 | ||
3.60-3.70 | 1.70-1.88 | 2.8-3.2 | |||
Y30 | 380-390 | 191-210 | 27-30 | ||
3.80-3.90 | 2.40-2.64 | 3.4-3.7 | |||
Y33 | 400-410 | 175-195 | 30.0-31.5 | C5 | |
4.00-4.10 | 2.20-2.45 | 3.8-4.0 | |||
Y35 | 410-420 | 220-235 | 31.5-33.0 | ||
4.10-4.20 | 2.77-2.95 | 4.0-4.2 | |||
Y30BH | 380-390 | 223-235 | 27.0-30.0 | C8 | |
3.80-3.90 | 2.80-2.95 | 3.4-3.7 | |||
Y33BH | 400-410 | 288-300 | 30.4-31.5 | ||
4.00-4.10 | 3.62-3.77 | 3.8-4.0 |